245 g/m2 Carbon - Epoxy Prepreg MTC510-C245T VWEAVE-HS-3K-42%RW Twill 2x2

MTC510 Carbon-epoxy prepreg is manufactured with a high tenacity epoxy resin prepared to cure between a variable temperature range of 80 ° C and 120 ° C. It is used to manufacture composite parts. The carbon twill fabric comes in a finish in which the diagonals, typical of twill weave, converge in the center of the sheet forming a V pattern.

Key Features & Benefits

• Weight: 245 g/m2
• Carbon type: 2 x 2 twill, 3K.
• Roll Width: 1250 mm.
• Epoxy resin weight content: 42%.
• Cure temperature from 80°C - 120°C
• Service temperatures up to 135°C after postcure.
• Low CTE and shrinkage.
• Work life at 20°C: 28 days.
• Storage life at -18°C: 12 months.
• Very low VOC content – no added solvents during manufacture.
• Excellent surface finish.

Storage & Out Life

The material should be kept frozen at -18°C. It must be kept sealed in a polythene bag which must not be opened until fully thawed to room temperature. If the material is not fully used, then the material must be resealed in the polythene bag to prevent moisture absorption.

Type of supply

245 g/m2 Carbon - Epoxy Prepreg MTC510-C245T VWEAVE-HS-3K-42%RW x 1 m2, supplied rolled in cardboard box

245 g/m2 Carbon - Epoxy Prepreg MTC510-C245T VWEAVE-HS-3K-42%RW x 5 m2, supplied rolled in cardboard box

245 g/m2 Carbon - Epoxy Prepreg MTC510-C245T VWEAVE-HS-3K-42%RW x 25 m2, supplied rolled in cardboard box