Round Carbon Fibre Tube, ext. ∅ 32 mm, int. ∅ 28 mm, 2 mm thickness (2000 mm length)
By buying this product you can collect up to 10 points. Your cart will total 10 points that can be converted into a voucher of €1.00.
Round carbon fibre tube manufactured by using the pultrusion technique in which the high-performance carbon fibres are all orientated in the axial direction (unidirectional) and internally reinforced with more unidirectional carbon fibre laminated by using pullwingding technology to achieve greater resistance to bending and torsion.
Round carbon fibre tube manufactured by using the pultrusion technique in which the high-performance carbon fibres are all orientated parallel to the longitudinal axis (unidirectional) and internally reinforced with more unidirectional carbon fibres laminated by using pullwingding technology to achieve greater resistance to bending and torsion.
Diameter: 32 mm; int. 28 mm
Length: 2000 mm (2m)
Thickness: 2 mm
This type of profile has a high specific mechanical resistance (related to its weight), lightness, rigidity, great resistance to fatigue and vibrations, resistance to oxidation and corrosion, low coefficient of thermal expansion and durability.
Pultrusion is a technique of continuous production of linear profiles with a constant section. This process has many similarities to extrusion, the main difference is in the feeding system: in extrusion the material is pushed through the matrix (mould), in pultrusion it is extracted from the matrix. This procedure does not allow variations in shape, sections or curves. Products that can be obtained by this process can have sections or thicknesses of up to approximately 15mm, with epoxy resins and up to 70mm with polyester resins.
Products made with this technology have excellent tensile strength characteristics due to the linear orientation of the fibres in the direction of axis of the profile; if it is also necessary to have a good transversal resistence, a woven fabric is used as a backing in specific quantities and weights.
Mechanical Resistances according to standard UNI EN 13706-1-2-3 ISO527
- Elastic module (E): 150 GPa
- Elastic module x section (E A): 28.274 kN
- Tensile strength > 2.463 MPa
- Tensile strength in section: 464 kN
Carbon Fibre Properties
- Number of filaments: 24K (24.000 filaments per strand)
- Elastic module (E): 234 GPa
- Tensile strength: 4.830 MPa
- Density: 1,80 g/cm3
- Carbon fibre content by volume (Vf): 68%
- Glass transition temperature (Tg), ISO 11357-2 DSC: 140 ºC
- Recommended Start Temperature : -30 ºC a + 100 ºC
- Resin type: epoxi
Caution: Pultruded carbon fibre materials are ellectrically conductive. if the material has been packed, be careful when removing / unwinding the film as the material could be under tension.
In case of being machined (cutting, sanding, drilling...), it is recommended to wear protective masks, glasses and gloves.