Crestafix 621CC 45 urethane acrylate / isophthalic polyester bonding paste
By buying this product you can collect up to 1 point. Your cart will total 1 point that can be converted into a voucher of €0.10.
The Crestafix 621CC range is a pre-accelerated urethane acrylate / isophthalic polyester high performance bonding paste. It is a non-sagging, filled compound, specifically designed for the assembly and bonding of GRP mouldings.
The Crestafix 621CC range is a pre-accelerated urethane acrylate / isophthalic polyester high performance bonding paste. It is a non-sagging, filled compound, specifically designed for the assembly and bonding of GRP mouldings. Such applications include panels, inserts, internal frames, ribs, internal core materials, composite constructions and car body components. All Crestafix 621CC products provide a high shear strength bonded joints without the need for mechanical fixings.
Features and Benefits
- Highly thixotropic: No drainage on vertical surfaces
- Colour change system:Visual check for effective catalyst mix
- Low shirnk system: No print through, excellent surface aspect
- Urethane acyrlate base: Excellent adhesion and good elogation at break
Geltime/ Working time for Crestafix 621 CC 45 at 25ºC for 100 g of bonding paste catalised with 3% by weight of Luperx K1S or X-8 Catalyst: 22-28 min
Gap Filling: 1-25 mm
Colour Change: Blue/green to grey
The surfaces to be bonded should be clean, dry and free from any contamination. It may be necessary to mechanically abrade the surfaces to be bonded in order to obtain the bond strength required. Each surface should be coated with the catalysed bonding paste and held together until the adhesive has hardened.
Crestafix 621CC are supplied pre-accelerated, requiring only the addition of catalyst to start the curing reaction. The recommended catalyst is Catalyst M (or Butanox M50 or other equivalent MEKP catalyst like Luperox K1S or X-8 Catalyst), which should be added at 1% to 2% w/v into the bonding paste. The catalyst should be thoroughly incorporated into the material with a low shear mechanical stirrer where possible, taking care to keep air entrapment to a minimum. Alternatively the bonding paste can be applied with a dispensing unit. The bonding paste, moulding and workshop should all be at, or above, 15°C before curing is carried out. Recommended temperature range for application is between 18°C and 25°C. The use of additional pigments or fillers is not recommended as they can affect the performance of the adhesive.For industrial/commercial use only. The user must determine the suitability of a selected adhesive for a given substrate and application. Contact your local Scott Bader representative for questions or assistance with the selection of adhesives for your use. This product is intended for use by skilled individuals at their own risk. Recommendations contained herein are based on information we believe to be reliable. The properties and strength values obtained under controlled conditions at the Scott Bader laboratory.
Shelf life: 6 month at room temperature of about 23 ºC.
Type of supply
Crestafix 621CC 45 x 1 kg, supplied with 20 g of MEKP
Crestafix 621CC 45 x 5 kg, supplied with 100 g of MEKP
Crestafix 621CC 45 x 25 kg, supplied with 0,5 kg of MEKP