RESOLCOAT 2060 GC ALU epoxy gelcoat is formulated for the production of composites tooling. It enables to manufacture tooling that will resist many years to the most demanding heating and cooling post-curing cycles of: heating RTM & pre-preg tooling, high output heat forming of thermoplastics or polymer concrete/solid surface injection tools. Maximum Tg: 115 ºC.
RESOLCOAT 2060 GC ALU epoxy gelcoat is formulated for the production of composites tooling. It enables to manufacture tooling that will resist many years to the most demanding heating and cooling post-curing cycles of: heating RTM & pre-preg tooling, high output heat forming of thermoplastics or polymer concrete/solid surface injection tools.
Its Novolac based formula guarantees the highest mechanical and chemical resistance, notably to styrene. Polyester or Vinylester parts manufactured on the 2060 GC ALU gelcoat will release with high gloss for numerous cycles. Should the gelcoat needed to be repaired, polishing the repaired area will enable to regain a high gloss surface aspect.
This new generation system, optimized with excellent self levelling characteristics and excellent air release, is suitable for the manufacture of large composite tooling. It should be applied by brush or airless.
The recommended application thickness ranges from 500 μm to 900 μm @ 25°C, which it is possible to achieve in one coat on a vertical surface without sag.
Final thermo-mechanical properties will be obtained after a post curing cycle defined according later in this technical data sheet.
Mixing ratio by weight = 100 : 13.
Gel time ( 300 g at 25 ° C ): 4 hours and 40 minutes with Hardener 2061S.
Demoulding time at 20 °C: After 24 hours at 23 ºC.
Maximum Tg after posturing process: 115 ºC.