MILLIFOAM TGC50R Polyphenylsulfone Foam (PPS), High Fire Resistance
MILLIFOAM TGC50R Polyphenylsulfone Foam (PPS), High Fire Resistance
MILLIFOAM TGC50R Polyphenylsulfone Foam (PPS), High Fire Resistance
MILLIFOAM TGC50R Polyphenylsulfone Foam (PPS), High Fire Resistance

MILLIFOAM® TGC50R-PF20 Polyphenylsulfone Foam (PPS), High Fire Resistance, for infusion

TGC50RPF20-1.0-1
3 Items
€54.33

By buying this product you can collect up to 5 points. Your cart will total 5 points that can be converted into a voucher of €0.50.

€54.33 Tax incl. €44.90 Tax excl.
Tax included

MILLIFOAM® TGC50R is a closed-cell, recyclable rigid polymer foam based on polyphenylsulfone (PPSU) chemistry. It offers excellent fire, smoke and toxicity (FST) properties for aerospace interior designs and exceeds FAR 25.853 requirements for flammability and HL3 requirements for R1 applications. Qualified by AIRBUS under AIMS 04-11-008 and ABS5927 standard for aircraft interior parts.

Supply

 Calculate Shipping Cost
Shipping:
0
to Spain via
Estimated delivery: No estimated delivery specified day(s)
Ratings and comments from our customers
( 0.0 / 5) - 0 feedback(s)

MILLIFOAM® TGC50R PF20 is an interesting alternative in weight critical applications, where vacuum bagging or prepreg techniques commonly are used. Due to the perforations it is possible to vacuum bag both inner and outer laminate in one operation, which yields cost and time savings in mentioned processes. It is suitable for a variety of processes including infusion, prepreg and press bonding.

Diameter of the drills/perforations: 2.5 mm

-------------------------

MILLIFOAM® TGC50R PF20 is a closed-cell, recyclable rigid polymer foam based on polyphenylsulfone (PPSU) chemistry. It offers excellent fire, smoke and toxicity (FST) properties for aerospace interior designs and exceeds FAR 25.853 requirements for flammability and HL3 requirements for R1 applications. The foam is qualified by AIRBUS under AIMS 04-11-008 and ABS5927 standard for aircraft interior parts. Its excellent low dielectric constant and transmission properties make it ideal for the use in antenna systems and radomes.

Polymer

PPSU

Sheet Size

2500 x 590 mm

Tolerance: +5/-25mm

Thickness range

1.0-6.0 mm

Supplier

4a manufacturing GmbH

MILLIFOAM® TGC50R can be cut, bonded and thermoformed without suffering from excessive spring-back or shrink. It withstands prolonged exposure to water, chemicals and temperatures ranging from -40°C to 204°C (-40°F to 400°F). As material in sandwich structures it is hot and cold formable and gives additionally freedom for design innovation. The thermoforming process window depends on geometry, applied stretching, thermoforming method and sheet thickness.

MILLIFOAM® TGC50R Properties*

Density

53 kg/m³

Compressive Strength

0.65 MPa

Compressive Modulus

23 MPa

Tensile Strength

1.1 MPa

Shear Strength

0.75 MPa

Shear Modulus

9.3 MPa

Dielectric constant @ 10GHz

1.015

Loss tangent @ 10GHz

0.0095

Coefficient of Thermal Expansion

4.2 1/K*10E-5

Thermoforming Temperature

205-230°C (401-446°F)

*Data refer to original vendor information

Type of Supply

MILLIFOAM® TGC50R1-1, thickness 1 mm (+10%) x sheets of 1250 mm x 590 mm

MILLIFOAM® TGC50R2-1, thickness 2 mm (+10%) x sheets of 1250 mm x 590 mm

MILLIFOAM® TGC50R3-1, thickness 3 mm (+10%) x sheets of 1250 mm x 590 mm

Supplied in a cardboard box.