Resoltech 1050 Infusion Epoxy Resin

The 1050 epoxy laminating system is formulated to manufacture high performance lightweight structures with glass, carbon, aramid and basalt reinforcements with or without post-curing.

This latest generation system, without CMR substances according to GHS criteria is optimized with a low exotherm, low viscosity and excellent air release properties. This epoxy system is also suitable for the manufacture of small to very large structures and composite parts by wet lay-up, infusion, injection moulding or filament winding while guaranteeing low toxicity working conditions to the users.

All hardeners mix with a 100/35 ratio and can be pre-blended together to precisely adjust the desired pot life. The 1050 resin + 1053S system is particularly recommended for infusion thanks to its low mixed viscosity (205 mPa.s).

Mixing ratio by weight: 100/35

Maximum Tg: 78 °C

Colour: Colorless Clear

To achieve semi flexible parts it´s possible to combine RESOLTECH 1050 and RESOLTECH 1600. More info here.

Type of supply

Resoltech 1050/1059S infusion epoxy resin x (1 + 0.35) kg, gel time of 13 minutes for 70 g at 23 °C 

Resoltech 1050/1059S infusion epoxy resin x (5 + 1.75) kg, gel time of 13 minutes for 70 g at 23 °C 

Resoltech 1050/1059S infusion epoxy resin x (25 + 8.75) kg, gel time of 13 minutes for 70g at 23 °C

Resoltech 1050/1058S infusion epoxy resin x (1 + 0.35) kg, gel time of 27 minutes for 70 g at 23 °C

Resoltech 1050/1058S infusion epoxy resin x (5 + 1.75) kg, gel time of 27 minutes for 70 g at 23 °C

Resoltech 1050/1058S infusion epoxy resin x (25 + 8.75) kg, gel time of 27 minutes for 70 g  at 23 °C

Resoltech 1050/1056S infusion epoxy resin x (1 + 0.35) kg, gel time of 38 min for 70 g at 23 °C

Resoltech 1050/1056S infusion epoxy resin x (5 + 1.75) kg, gel time of 38 min for 70 g at 23 °C

Resoltech 1050/1056S infusion epoxy resin x (25 + 8.75) kg, gel time of 38 min for 70 g at 23 °C

Resoltech 1050/1055S infusion epoxy resin x (1 + 0.35) kg, gel time of 2 h 37 min for 70 g at 23 °C

Resoltech 1050/1055S infusion epoxy resin x (5 + 1.75) kg, gel time of 2 h 37 min for 70 g at 23 °C

Resoltech 1050/1055S infusion epoxy resin x (25 + 8.75) kg, gel time of 2 h 37 min for 70 g at 23 °C

Resoltech 1050/1053S infusion epoxy resin x (1 + 0.35) kg, gel time of 14 hours for 70 g at 23 °C

Resoltech epoxy resin 1050/1053S x (5 + 1.75) kg, gel time of 14 hours for 70 g at 23 °C

Resoltech 1050/1053S infusion epoxy resin x (25 + 8.75) kg, gel time of 14 hours for 70 g at 23 °C