215 gsm Carbon-Aramid Epoxy Prepreg MTC510-CK215T-45%RW-1000 Twill 3x1

MTC510 Carbon-epoxy prepreg is manufactured with a high tenacity epoxy resin prepared to cure between a variable temperature range of 80 ° C and 120 ° C. It is used to manufacture composite parts.

Key Features & Benefits

• Weight: 215 g/m2
• Type of weave: twill 3x1
• Type of yarns: Kevlar® 49 T 968 / T 968 TG + Carbon 3K (1:1) of 127 + 200 Tex.
• Roll Width: 1000 mm.
• Thickness: 0.37 mm
• Epoxy resin weight content: 45%.
• Cure temperature from 80°C - 120°C
• Service temperatures up to 135°C after postcure.
• Low CTE and shrinkage.
• Out life at 20°C: 28 days.
• Shelf life at -18°C: 12 months.
• Very low VOC content – no added solvents during manufacture.
• Excellent surface finish.

Storage & Out Life

The material should be kept frozen at -18°C. It must be kept sealed in a polythene bag which must not be opened until fully thawed to room temperature. If the material is not fully used, then the material must be resealed in the polythene bag to prevent moisture absorption.

Type of supply

215 g/m2 Carbon-Aramid Epoxy Prepreg MTC510-CK215T-45%RW x 1 m2, supplied rolled in cardboard box

215 g/m2 Carbon-Aramid Epoxy Prepreg MTC510-CK215T-45%RW x 5 m2, supplied rolled in cardboard box

215 g/m2 Carbon-Aramid Epoxy Prepreg MTC510-CK215T-45%RW x 25 m2, supplied rolled in cardboard box