RESOLTECH 1080S is the highest modulus epoxy system formulated to manufacture high performance, rigid, lightweight structures with glass, carbon, aramid and basalt fibres with or without post-curing. Optimized with a low reactivity, low viscosity and excellent air release properties, is suitable for the manufacture any size structures and composite parts by hand layup, infusion and RTM.
RESOLTECH 1080S is the highest modulus epoxy system formulated by RESOLTECH to manufacture high performance, rigid, lightweight structures with glass, carbon, aramid and basalt fibres with or without post-curing.
Using this novolac based epoxy resin will enable to reduce the amount of reinforcement fibre used, resulting in lighter, more rigid but also cheaper parts in spite of its higher price compared to more common Bisphenol A & F based resins.
This new generation system, optimized with a low reactivity, low viscosity and excellent air release properties, is suitable for the manufacture any size structures and composite parts by hand layup, infusion and injection moulding while guaranteeing low toxicity working conditions to the user and ease of use thanks to its high wetting properties.
It features an adjustable working time from 2h30 to 8h30 with its range of hardeners.
It is possible to release the parts from the mould without postcuring. The maximum thermo mechanical properties of the laminate will be obtained after a postcuring cycle to obtain a final Tg of 110 ºC.
RESOLTECH 1080S is recommended for the production of marine foils, secondary laminations of chain plates, production of lightweight & rigid skiffs or high performance kayaks & outriggers where the weight/rigidity is key.
The 1080S is used on many Dakar wining rally cars, all types of RC models but also for the production of helicopter, gyrocopter & airplane propellers.
Gel time with 1082: 8 h 33 min at 23 °C for 50 g mixture
Gel time with 1084: 2 h 3 min at 23 °C for 50 g mixture
Color: Colorless with a slightly yellowish hue
Type of supply
Resoltech 1080S (1 kg) + 1082 (0,33 kg), gel time of 8 h 33 min
Resoltech 1080S (5 kg) + 1082 (1,65 kg), gel time of 8 h 33 min
Resoltech 1080S (27 kg) +1082 (8,91 kg), gel time of 8 h 33 min
Resoltech 1080S (1 kg) + 1084 (0,33 kg), gel time of 2 h 30 min
Resoltech 1080S (5 kg) + 1084 (1,65 kg), gel time of 2 h 30 min
Resoltech 1080S (27 kg) + 1084 (8,91 kg), gel time of 2 h 30 min
- Heat resistance
- Between 75 and 120ºC
- Processing time
- Above 2 hours
Above 8 hours - UV resistance
- No
- Colour
- Slightly yellowish
- Flexible
- No